Epoxy Antistatic Coating For Use In Interior Wall of Oil Tank and
Steel Pipes Antistatic Anticorrosive
-A two pack epoxy antistatic coating
-VOC less than 280g/L
-For use in interior wall of oil tank and steel pipes antistatic
|Typical Film Thickness||125microns dry (167microns wet)|
|Theoretical Coverage||6m2/L at typical film thickness|
|Method of Application|
|Tip size range|
|Air Spray||Tip size range||2.0-3.0mm|
|Brush/Roller||For small area only|
|Thinner||Not recommended. Use only in exceptional circumstances (volume 5%)|
|Induction Period||Not necessary|
|Overcoating Data Substrate Temperature|
|Min Max||Min Max||Min Max|
|36h 10d||24h 7d||16h 5d|
|Storage||Store in cool and dry conditions. Well ventilate. Keep away from
hot and fire. Shelf Life: 12 months minimum at 25℃. Subject to
|Pack Size||Part A||28kg/16.5L in 20 L container|
|Part B||3.5kg/3.5L in 6L container|
|Flash Point||Part A||Greater than 31℃|
|Part B||Greater than 28℃|
|Mixed paint||Greater than 31℃|
All surfaces to be coated should be clean, dry and free from
Abrasive Blast Cleaning
Abrasive blast clean to Sa2½(GB/T 8923.1-2011). If oxidation has
occurred between blasting and application of 725-H58-06, the
surface should be reblasted to the specified visual standard.
Surface defects revealed by the blast cleaning process should be
ground. Filled, or treated in the appropriate manner.
Metallic Zinc Primed Surfaces
Ensure that surface of the primer is clean, dry and free from
contamination and zincsalts before application of 725-H58-06.
Ensure zinc primers are fully cured beforeovercoating.
The areas to be repaired should be cleaned to St3(GB/T
8923.1-2011)by mechanical method or higher level of surface
prepared to Sa2.5(GB/T 8923.1-2011)by abrasive blasting. Abrade the
area immediately surrounding the repair to provide a key for
subsequent coating application. Overlap areas should be kept to a
This product will not cure adequately below 5℃. For maximum
performance ambient curing temperature should be above 10℃.
In common with all epoxy base coatings, 725-H58-06 will exhibit
chalking of the firm on UV exposure.
Apply in good weather. Temperature of the surface to be coated must
be least 3℃ above the dew point when the humidity is lower than
The dry time and overcoating interval may change according to the
Avoiding absorb the solvent steam and paint steam for long time.
Skin and eyes must avoid contacting the paint. Pay attention to
ventilate and fireproof when applying.
|The data in the sheet base on the information from the laboratory